Properties of UV-curable screen printing inks containing oligolactide acrylates

ผู้แต่ง

  • Santi Kulsiriswad Faculty of Science, Chulalongkorn University
  • Onusa Saravari Faculty of Science, Chulalongkorn University
  • Kawee Srikulkit Faculty of Science, Chulalongkorn University and Center of Excellence on Petrochemical and Materials Technology, Chulalongkorn University

คำสำคัญ:

Weathering resistance, Oligolactide acrylate, UV-curable, Printing ink

บทคัดย่อ

This study was aimed at investigating the properties of UV-curable screen printing inks prepared from oligolactide acrylates. Those resultant inks were applied on substrates and cured by UV radiation. Then, properties of the cured ink films were evaluated and compared with a commercial acrylate ink. The degradation temperature of ink film was found at around 436°C. In addition, thus obtained films were glossy and transparent without yellowness. The weathering resistance of ink films tested by a Xenon test chamber for 500 h showed that ink films exhibited acceptable outdoor durability. Discoloration due to the degradation of lactide chain was observed, albeit color differences (∆E) were satisfactorily less than 1. When compared to a commercial polyester acrylate ink, the prepared inks exhibited comparable properties. As a result, these prepared inks are commercially possible for substituting non biodegradable commercial inks particularly outdoor applications.

Downloads

Download data is not yet available.

เอกสารอ้างอิง

J. Izdebska and S. Thomas, Printing on polymers: fundamentals and applications. William Andrew, 2015.

Z. W. Wicks, F. N. Jones, S. P. Pappas, and D. A. Wicks, Organic coatings: science and technology, 3rd ed. New Jersey, USA: John Wiley & Sons, 2007.

J. A. Arceneaux, "UV/EB chemistry and technology," RadTech International, 2016.

P. Chittavanich, K. Miller, and M. Soucek, "A photo-curing study of a pigmented UVcurable alkyd," Progress in Organic Coatings, vol. 73, no. 4, pp. 392-400, 2012.

J. V. Crivello and K. Dietliker, "Chemistry & technology of UV & EB formulation for coatings, inks & paints," in Volume 3: Photoinitiators for free radical cationic & anionic photopolymerisation, G. Bradley, Ed., 2nd ed., Chichester: J. Wiley, 1998.

C. Lowe, G. Webster, S. Kessel, and I. McDonald, Chemistry & Technology for UV & EB Formulation for Coatings, Inks & Paints, Formulation. Wiley, 1997.

R. Leach, The printing ink manual. New York, USA: Springer Science & Business Media, 2012.

K.R. Miller and M.D. Soucek, "Photopolymerization of biocompatible films containing poly (lactic acid)," European Polymer Journal, vol. 48, no. 12, pp. 2107-2116, 2012.

S. Cheng, H. Zhou, D. R. Fenn, and J. L. Kulfan, "Radiation curable coating compositions comprising a lactide reaction product," Patent 9,650,540, 2017, May 16 2017.

S. Kulsiriswad, K. Srikulkit, and O. Saravari, "An oligolactide acrylate for UV-curable screen printing inks," Journal of Engineering and Applied Sciences, vol. 11, no. 12, pp. 2775-2780, 2016.

S. Kulsiriswad, K. Srikulkit, and O. Saravari, "Effects of the Amount and Type of Diol Ring Openers on the Properties of Oligolactide Acrylates for UV-Curable Printing Inks," Coatings, vol. 7, no. 10, p. 174, 2017.

R. Schwalm, UV coatings: basics, recent developments and new applications. Amsterdam, London: Elsevier, 2007.

G. Bayramoğlu, M. V. Kahraman, N. Kayaman-Apohan, and A. Güngör, "The coating performance of adipic acid modified and methacrylated bisphenol A based epoxy oligomers," Polymers for Advanced Technologies, vol. 18, no. 3, pp. 173-179, 2007.

V. Thalacker and T. Boettcher, "Thermal stability of radiation curable materials," Radiation Physics and Chemistry (1977), vol. 25, no. 1, pp. 323-332, 1985.

A. Goswami, G. Srivastava, A. Umarji, and G. Madras, "Thermal degradation kinetics of poly (trimethylol propane triacrylate)/poly (hexane diol diacrylate) interpenetrating polymer network," Thermochimica Acta, vol. 547, pp. 53-61, 2012.

M. Opaprakasit, A. Petchsuk, P. Opaprakasit, and S. Chongprakobkit, "Effects of synthesis conditions on chemical structures and physical properties of copolyesters from lactic acid, ethylene glycol and dimethyl terephthalate," Express Polymer Letters, vol. 3, no. 7, pp. 458-468, 2009.

A. Musidang and N. Jiratumnukul, "Preparation of poly (Lactic acid) acrylate for UV-curable coating applications," Key Engineering Materials, vol. 659, pp. 570- 574, 2015.

C. Decker and S. Biry, "Light stabilisation of polymers by radiation-cured acrylic coatings," Progress in Organic Coatings, vol. 29, no. 1-4, pp. 81-87, 1996.

M. Gardette, S. Thérias, J.-L. Gardette, M. Murariu, and P. Dubois, "Photooxidation of polylactide/calcium sulphate composites," Polymer Degradation and Stability, vol. 96, no. 4, pp. 616-623, 2011.

D. K. Wang, S. Varanasi, P. M. Fredericks, D. J. Hill, A. L. Symons, A. K. Whittaker, and F. Rasoul, "FT-IR characterization and hydrolysis of PLA -PED-PLA based copolyester hydrogels with short PLA segments and a cytocompatibility study," Journal of Polymer Science Part A: Polymer Chemistry, vol. 51, no. 24, pp. 5163-5176, 2013.

J. F. Gonnet, "Colour effects of co - pigmentation of anthocyanins revisited—2. A colorimetric look at the solutions of cyanin co-pigmented byrutin using the CIELAB scale," Food Chemistry, vol. 66, no. 3, pp. 387-394, 1999.

ดาวน์โหลด

เผยแพร่แล้ว

2019-01-10

วิธีการอ้างอิง

[1]
S. Kulsiriswad, O. Saravari, และ K. Srikulkit, “Properties of UV-curable screen printing inks containing oligolactide acrylates”, J Met Mater Miner, ปี 28, ฉบับที่ 2, ม.ค. 2019.

ฉบับ

บท

Original Research Articles

Most read articles by the same author(s)

1 2 > >>