Structure and Properties of Thin Layer – Substrate on High Speed Steel with Different Thickness of TiN

Authors

  • Mária Hagarová Department of Materials Science, Faculty of Metallurgy, Technical University of Košice

Keywords:

TiN coating, PVD technology, hardness, scratch test

Abstract

The main application of TiN coating deposited on metallic materials by Arc – PVD method is to increase the wear resistance. The properties of TiN coating are related to the properties of the substrate, technological parameters, microstructure, thickness, adhesion and hardness of the film. This paper presents the results of mechanical property measurement of 2 mm and 4 mm thick TiN coatings deposited on high-speed steel. The hardness was measured by nanoindentor and the adhesion by scratch test. The microstructure of TiN coating was evaluated by SEM microscopy.

Downloads

Download data is not yet available.

References

Hagarová, M. 2003. Thesis, Faculty of Metallurgy, Technical University in Košice,

Jakubéczyová, D and Fáberová, M. 2003. Možnosti povrchovej úpravy P/M nástrojových ocelí. Metal : 1 – 7

ISO/DIS 14577, 2001. Metallic materials – Instrumented indentation test for hardness and materials parameters,

Ballo, V. 1998. Doctoral, Thesis, Faculty of Metallurgy, Technical University in Košice,

Downloads

Published

2022-08-19

How to Cite

[1]
M. Hagarová, “Structure and Properties of Thin Layer – Substrate on High Speed Steel with Different Thickness of TiN”, J Met Mater Miner, vol. 15, no. 2, pp. 39–43, Aug. 2022.

Issue

Vol. 15 No. 2 (2005)

Section

Original Research Articles

License

Copyright (c) 2005 The Journal of Metals, Materials and Minerals (JMMM)

Creative Commons License

This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Authors who publish in this journal agree to the following terms:

    1. Authors retain copyright and grant the journal right of first publication with the work simultaneously licensed under a Creative Commons Attribution License that allows others to share the work with an acknowledgment of the work's authorship and initial publication in this journal.

 

    1. Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgment of its initial publication in this journal.