Fractures of as-cast low-carbon steels in the plasticity degradation area at high testing temperatures
DOI:
https://doi.org/10.55713/jmmm.v16i1.246Abstract
The work studies the fractures of low-carbon steels after tensile tests in a temperature interval from ca 1200°C, where a plasticity degradation takes place, up to the liquid phase formation temperature. Statistical analyses of the temperature dependence of the reduction of area were made with the aim to determine integral effects of the chemical composition on the plasticity course.
In the plasticity degradation temperature area, intercrystalline fractures occur, which have several morphologies, even within the same steel grade. Besides typical intercrystalline fractures, a fine-grained, interdendritic fracture often occurs. A specific case is the failure of steels in the γ + δ two-phase area, where fractures are formed at the phase interface. According to the failure type, fractures have been classified under 4 basic groups.
The fracture process and subsequently the plasticity degradation temperature and the plasticity course are determined by the intensity of decohesion of polygonal boundaries of austenite grains, or δ-ferrite grains, and of boundaries of interdendritic space. With increasing content of phosphorus, which segregates on the polygonal grain boundaries, the plasticity degradation start temperature decreases. At the highest testing temperatures, phosphorus degrades the cohesive strength of grain boundaries by formation of a liquid phase.
The slope of the temperature dependence of plasticity degradation and the temperature of plasticity degradation to a nearly non-measurable level, th5, are mainly determined by the Al/N ratio. An increase of the Al/N ratio, which was in the interval from 2.2 to 16 for the tested steels, shifts the th5 temperature to the right.Downloads
References
(1) Mintz, B. 1999, ISIJ Int. 39 : 833 – 855.
(2) Sricharoenchai, P.Nagasaki, C. and Kihara, J. 1992. ISIJ Int.32 : 1102 – 1109.
(3) Nagasaki, C. and Kihara, J. 1997. ISIJ Int.37 : 523 – 530.
(4) Won, Y. M. and Thomas, B. G. 2001. Met. Trans. A. 32A : 1755 – 1768.
(5) Gao, Y. and Sorimachi, K. 1995. ISIJ Int.35 : 914 - 919.
(6) Yoshida, N., Umezawa, O. and Nagai, K. 2003. ISIJ Int.43 : 348 - 357.
(7) Yin,H., EMI, T. and Shibata, H. 1999. Acta Mater.47 : 1523 – 1535.
(8) Phelan, D. and Dippenaar, R. 2004. ISIJ Int. 44: 414 – 421
(9) Matsuoka H, et al. 1997. ISIJ Int. 37 : 255 – 262.
(10) Mazanec, K. 1988. Kovové Materiály. 26 : 5 – 50.
(11) Grabke, H.J. 1989. ISIJ Int.29 : 529-538.
(12) Yu, C.H., Suzuki, M.and Shibata, H. 1996. ISIJ Int.36 : Supplement S159 - S162.
(13) Gao, Y. and Baker, T. N. 1998. ISIJ Int.38 : 744 – 751.
(14) Easterling K 1992. Physical Metallurgy of Welding. London , Butterworths : 122
(15) Yoshida, N., Umezawa, O.and Nagai, K. 2004 ISIJ Int.44 : 547 – 555.
(16) Ode, M. et al. 2001. ISIJ Int.41 : 345 – 349.
(17) Ševčík, A. and Ševčíková, J. 2005. Acta Metallurgica Slovaca.11 : 36 – 44.
(18) Ševčík, A. and Ševčíková, J. 2005. Transactions of the Universities of KošiceNo 1 : 48 – 53.
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2017 Journal of Metals, Materials and Minerals
This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.
Authors who publish in this journal agree to the following terms:
- Authors retain copyright and grant the journal right of first publication with the work simultaneously licensed under a Creative Commons Attribution License that allows others to share the work with an acknowledgment of the work's authorship and initial publication in this journal.
- Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgment of its initial publication in this journal.