Zn coatings for temporary protection applied by peening technology


  • Janette Brezinnová Mechanical Engineering Faculty, Technical University


Zn coating, surface protection, peening technology


This paper presents actual investigation results of an experiment that aimed at verifying the possibility of applying zinc on steel surface by peening technology using zinc-coated cut wire. A suitable method for obtained zinc layers and evaluation of their corrosion resistance was determined. Accelerated laboratory tests with presence of SO2 and long term working tests in atmospheric conditions were used. Creation of incoherent zinc coatings was established on the bases of metallographic and spectral analysis. The process of cold zinc by peening may serve as temporary anticorrosion protection of steel surface.


Download data is not yet available.


Kalendová, A. et al. 2003. Acta Mechanica Slovaca. 4-A : 97-102.

Kniewald, D., Brezinová, J. 2003. 35th International Conference on Coatings Technology. ČR, Pardubice. : 489-496.

Kováč, J. et al. 2002. Corrosion and protection of material. 5 : 103-107.

.Kalendová, A. 1998. Anticorrosive spinel-type pigments of the second gener. AntiCorrosion Methods Mater. 45 : 344-349.

Kováč, J., Brezinová, J., Kniewald, D. 2001. Acta Metallurgica Slovaca. 7(2) : 177-183.

.Skočovský, P. et al. 2001. Theory about material for engineering specialization. University of Žilina. : 167-171.

Zerust Worldwide Corrosion Prevention. www.fatrani.cz

Kalenda, P. et al. 2005. Acta Mechanica Slovaca. 9(3) : 93-98.

Brezinová, J. 2002. The study of blasting process regularity from the aspect of degradation phenomenons. Master Thesis. Technical University of Košice.

Kalendová, A. et al. 2005. CHEMagazín. No.1 : 24-27.

Kniewald, D., Brezinová, J. 2003. Study of process cold zinc by peening, CO-MATTECH Trnava : 485-488.

Brezinnová J. 2003. Acta Mechanica Slovaca. No.4-A : 29-32.




How to Cite

J. Brezinnová, “Zn coatings for temporary protection applied by peening technology”, J Met Mater Miner, vol. 17, no. 2, Apr. 2017.



Original Research Articles