Formation of Phase Icosahedral and Decagonal Quasicrystalline AlloysAl62,2Cu25,3Fe12,5/Al65Ni15Co20 Influence on The Oxidation
คำสำคัญ:
quasicrystals, phases, icosahedral, decagonal, aluminum oxideบทคัดย่อ
In this article we will cover a study of the formation of icosahedral and decagonal phases two quasicrystals Al62,2Cu25,3Fe12,5 And Al65Ni15Co20,and the influence of oxidation in this alloy. For this purpose research used the diffraction of X-ray (XRD), scanning electron microscopy (SEM)/Energy Dispersive Spectroscopy (EDS), Differential Scanning Calorimetry (DSC) and Thermogravimetric Analysis (TG) .The results displayed found aspects of morphological structural as well as the surface of the two compositions of quasicrystals, these were prepared and obtained in electric arc furnaces and induction and arc. Oxidation of Al62,2Cu25,3Fe12,5 alloy, intermetallic phases presented with combinations of alloying elements and above 675°C it was observed that the crystalline phase is stable. In icosahedral phase oxidation of aluminum forms a dense layer on the passivating outermost surface of the quasicrystal which causes depletion in both copper and iron.In Al65Ni15Co20 nominal composition of oxygen interaction occurs on the surface of symmetry 10 times plane perpendicular vector .The formation of a thin film of aluminum oxide having well-ordered hexagonal structure and with the opposition area decagonal phase with the lateral size of approximately 35 Å.
Keywords: quasicrystals; phases; icosahedral; decagonal; aluminum oxide
Downloads
เอกสารอ้างอิง
Shechtman, D., Blech, I., Gratias, D. and Cahn, J.W. (1984). Metallic phase with long-range orientational order and no translational symmetry. Phys. Rev. Lett., 53 : 1951-1953.
Bonasso, N. and Pigeat, P. (2003). Preparation of Al-Cu-Fe ultra-thin quasicrystalline films without protective coatings by MBE: influence of processing. Mater. Sci. Eng., A 349 : 224-229.
Srivastava, V.C., Huttunen-Rivirta, E., Cui, C., Uhlenwinkel, V., Schulz, A., and Mukhopadhyay, N.K. (2014). Bulk synthesis by spray forming of Al–Cu–Fe and Al–Cu–Fe–Sn alloys containing a quasicrystalline phase. J. Alloys Compd. 597 : 258–268.
Rosas, G. and Perez, R. (2001). On the transformations of the ψ -AlCuFe icosahedral phase. Mater. Lett. 47 : 225–230.
Tsai, A. (2008). Icosahedralclusters,icosahedral order and stability of quasicrystalsa view of metallurgy. Sci. Technol. Adv. Mater. 9 : 1-21.
Yurechko, M., Grushko, B., Ya, T. and Velikanova, K. (2004). URBAN. A comparative study of the Al–Co–Pd and Al–Co–Ni alloy systems. J. Alloys Compd. 367 : 20–24.
Xinb, L., Yoshiaki, O., Susumu, T. and Gencang, Y. (2007). Thermal stability of decagonal quasicrystal prepared from undercooled Al72Ni12Co16 alloy melt. Mater. Lett. 61 : 5164–5168.
Wehner, B.I., Meinhardt, J., Köster, V., Alves, H., Eliaz, N. and Eliezer, D. (1997). Oxidation hydrogenation of quasicrystals. Mater. Sci. Eng., A 226-228 : 1008-1011.
Rouxel, D., Gil-Gavaltz, M., Pigeat, P. and Weberg, B. (2005). Oxidation kinetics of the quasicrystalline i-AlCuFe phase compared with that of crystalline ω -AlCuFe and pure aluminum. J. Non– Cryst. Solids. 351 : 802 – 809.
Chang, S.L., Anderegg, J.W. and Thiel, P.A. (2003). J. Non-Cryst. Solids. 195 : 95.
Burkardt, S., Erbudak, M. and Mäder, R. (2009). High-temperature surface oxidation of the decagonal AlCoNi quasicrystal. Surf. Sci. 603 : 867–872.
Dubois, J.M., Jeevan, H.S. and Rrnganathan, S. (1998). Quasicrystals, Ed. S. Takeuchi & T. Fujiwara, (Singapore: World Science).
Gogebakana, M., Avar, B. and Tarakci, M. (2011). Microstructures and mechanical properties of conventionally solidified Al63Cu25Fe12 alloy. J. Alloys Compd. 509(S) : 316–319.
Surowiec, M., Bogdanowicz, W. and Sozanska, M. (2014). Evolution of the Phase β Flux Dissolution during Quasicrystal Formation.Acta Physica. Polonica A 126 : 594-595.
Xinbao, L., Yoshiaki, O., Susumu, T. and Gencang, Y. (2007). Thermal stability of decagonal quasicrystal prepared from undercooled Al72Ni12Co16 alloy melt. Mater. Lett. 61 : 5164–5168.
Wehner, B.I. and Koster, U. (2000). Microstructural Evolution of Alumina Layers on an Al–Cu–Fe Quasicrystal during High-Temperature Oxidation. Oxid. Met. 54 : 5/6.
Parka, J.Y., Ogletree, D.F., Salmeron, M., Jenks, C.J. and Thiel, P.A. (2004). Friction and adhesion properties of clean and oxidized Al–Ni–Co decagonal quasicrystals: a UHV atomic force microscopy/scanning tunneling microscopy study. Tribol. Lett. 17(3).
Yurechko, M., Grushko, B., Ya, T., Velikanova, K. and Urban, A. (2004) comparative study of the Al–Co–Pd and Al–Co–Ni alloy systems. J. Alloys Compd. 367 : 20–24.
Rebecca, D., Haoxue, Y. and Ying, C. (2016). Grain boundary engineering of Co–Ni–Al,Cu– Zn–Al, and Cu–Al–Ni shape memory alloys by intergranular precipitation of a ductile solid solution phase. Scr. Mater. 115 : 113–117.
ดาวน์โหลด
เผยแพร่แล้ว
วิธีการอ้างอิง
ฉบับ
บท
การอนุญาต
ลิขสิทธิ์ (c) 2017 วารสารโลหะ, วัสดุ และแร่
This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.
Authors who publish in this journal agree to the following terms:
- Authors retain copyright and grant the journal right of first publication with the work simultaneously licensed under a Creative Commons Attribution License that allows others to share the work with an acknowledgment of the work's authorship and initial publication in this journal.
- Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgment of its initial publication in this journal.