Surface modification of polyester fabrics with vinyltriethoxysilane

ผู้แต่ง

  • Boonsri Kusuktham Faculty of Textile Industries, Rajamangala University of Technology Krungthep

คำสำคัญ:

Polyester, Fabric, Water-repellent, Vinyltriethoxysilane

บทคัดย่อ

Surface modification of polyester fabrics was studied aiming at improving the water repellency property. Vinyltriethoxysilane (VTES) was employed as surface modifying agent. Prior to application, VTES was prepared in aqueous emulsion using cetyltrimethylammoniun bromide (CTAB) as an emulsifying agent. The application of VTES emulsion was carried out using a padder and followed by curing at 150ºC for 15 minutes. The result showed that the treated fabrics exhibited higher contact angle values when compared to untreated fabric, indicating an increase in water repellency property. It was believed that VTES was converted into silicone through siloxane network. The presence of a silicone particle on the fabric surface led to an increase in surface roughness, attributing to an increase in hydrophobicity of the treated fabric.

##plugins.generic.usageStats.downloads##

##plugins.generic.usageStats.noStats##

เอกสารอ้างอิง

Nunn, D.M. (1979). The dyeing of synthetic-polymer and acetate fibre. West Yorkshire: Dyers Company Publications Trust.

Dadashian, F., Montazer, M. & Ferdowsi, S. (2010). Lipases improve the grafting of poly (ethylene terephthalate) fabrics with acrylic acid. J. Appl. Polym. Sci. 116(1) : 203-209.

Hassan, M.S, Atteia, R.M. & Zohdy, M.H. (2009). Metal complexes of natural and synthetic fabrics grafted with vinyl monomers by gamma irradiation. Polym. Composite 30(9) : 1283-1289.

Bech, L., Meylheuc, T., Lepoittevin, B. & Roger, P. (2007). Chemical surface modification of poly(ethylene terephthalate) fibers by aminolysis and grafting of carbohydrates. J. Polym. Sci. Pol. Chem. 45(11) : 2172- 2183.

Salomone, J.C. (1996). Polymeric materials encyclopedia (Vol. 10). Boca Raton: CRC Press: 7636-7639.

Cazacu, M., Dragan, S. & Vlad, A. (2003). Organic-inorganic polymer hybrids and porous materials obtained on their basis. J. Appl. Polym. Sci. 88(8) : 2060-2067.

Shieh, Y.T. & Liu, C.M. (1999). Silane grafting reactions of LDPE, HDPE, and LLDPE. J. Appl. Polym. Sci. 74(14) : 3404-3411.

Yin, W., Li, J., Wu, J. & Gu, T. (1997). Silicon secondary crosslinked IPN based on poly(methyl acrylate-co-acrylic acid) and SiO2. J. Appl. Polym. Sci. 64(5) : 903-909.

Oyman, Z.O. & Tinçer, T. (2003). Melt blending of poly(ethylene terephthalate) with polypropylene in the presence of coupling agent. J. Appl. Polym. Sci. 89(4) : 1039-1048.

ดาวน์โหลด

เผยแพร่แล้ว

2017-04-15

วิธีการอ้างอิง

[1]
B. . Kusuktham, “Surface modification of polyester fabrics with vinyltriethoxysilane”, J Met Mater Miner, ปี 20, ฉบับที่ 2, เม.ย. 2017.

ฉบับ

ปีที่ 20 ฉบับที่ 2 (2010)

บท

Original Research Articles

การอนุญาต

ลิขสิทธิ์ (c) 2017 Journal of Metals, Materials and Minerals

Creative Commons License

This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Authors who publish in this journal agree to the following terms:

    1. Authors retain copyright and grant the journal right of first publication with the work simultaneously licensed under a Creative Commons Attribution License that allows others to share the work with an acknowledgment of the work's authorship and initial publication in this journal.

 

    1. Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgment of its initial publication in this journal.