Effect of chromium content on the three-body-type abrasive wear behavior of multi-alloyed white cast iron
คำสำคัญ:
Multi-alloyed white cast iron, Hardness, Retained austenite, Three-body-type abrasive wear behavior, Cr effectบทคัดย่อ
The effect of Cr content on three-body-type abrasive wear behavior of multi-alloyed white cast iron was investigated. Multi-alloyed white cast irons were prepared with varying Cr content from 3-9 mass% under basic alloy composition. Annealed specimens were hardened from 1323 and 1373K austenitizing and tempered at three levels of temperatures which were at maximum hardness (HTmax), lower and higher than that at HTmax (L-HTmax and H-HTmax). A rubber wheel wear tester was used to evaluate the abrasive wear resistance. The hardness and volume fraction of the retained austenite (Vγ) varied depending on Cr content and heat treatment condition. The linear relation between wear loss and wear distance was obtained in all specimens. In each heat treatment condition, the wear rate (Rw) value decreased to 6 mass%Cr, and then, increased gradually as Cr content increased. As-hardened specimens showed higher wear resistance than tempered specimens did. In tempered state, the lowest Rw was obtained in HTmax specimen and the highest in L-HTmax or H-HTmax specimens. The Rw lowered greatly as the macro-hardness rose to 830 HV30, and after that it decreased continuously as the hardness increased. Moreover, Rw scattered broadly at Vγ lower than 5%, and then, decreased gradually as Vγ rose.Downloads
เอกสารอ้างอิง
H.-Q. Wu, N. Sasaguri, Y. Matsubara, and M. Hashimoto, "Solidification of multi-alloyed white cast iron : Type and morphology of carbides," AFS Transactions, vol. 140, pp. 103-108, 1996.
M. Hashimoto, "Development of multicomponent white cast iron (HSS) rolls and rolling technology in steel rolling," Abrasion Wear Resistant Alloyed White Cast Iron for Rolling and Pulverizing Mills, pp. 1-23, 2008.
Y. Matsubara, N. Sasaguri, and M. Hashimoto, "The history and development of cast rolls for hot working mill," The 4th Asian Foundry Congress-Australia, pp. 251-261, 1996.
M. Boccalini Jr., "Overview : High speed steels for hot rolling mill rolls," Abrasion Wear Resistant Alloyed White Cast Iron for Rolling and Pulverizing Mills, pp. 123-142, 2011.
I. R. Sare and B. K. Arnold, "The influence of heat treatment on the high-stress abrasion resistance and fracture toughness of alloy white cast irons," Metallurgical and Materials Transactions A, vol. 26, no. 7, pp. 1785-1793, 1995.
G. Laird, R. Gundlach, and K. Rohrig, Abrasion-Resistance Cast Iron Handbook. USA: American Foundry Society, 2000.
J. D. Watson, P. J. Mutton, and I. R. Sare, "Abrasive wear of white cast irons," Australian Institute of Metals Forum, vol. 3, pp. 74-88, 1980.
K.-H. Zum Gahr and D. V. Doane, "Optimizing fracture toughness and abrasion resistance in white cast irons," Metallurgical Transactions A vol. 11, no. 4, pp. 613-620, 1980.
S. Ma, J. Xing, Y. He, Yefei Li, Z. Huang, G. Liu, and Q. Geng, "Microstructure and crystallography of M7C3 carbide in chromium cast iron," Materials Chemistry and Physics, vol. 161, pp. 65-73, 2015.
O. Kubo, M. Hashimoto, and Y. Matsubara, "Influence of microstructure on wear resistance and crack propagation characteristics required for white iron rolling mill rolls," Proceedings of The Science of Casting and Solidifications, 2001.
J. Opapaiboon, P. Sricharoenchai, S. Inthidech, and Y. Matsubara, "Effect of carbon content on heat treatment behavior of multi-alloyed white cast iron for abrasive wear resistance," Materials Transections, vol. 56, no. 5, pp. 720-725, 2015.
W. Khanitnantharak, M. Hashimoto, K. Shimizu, K. Yamamoto, N. Sasaguri, and Y. Matsubara, "Effects of carbon and heat treatment on the hardness and austenite content of a multi-component white cast iron," AFS Transactions, vol. 117, pp. 435- 444, 2009.
M. Hashimoto, O. Kubo, and Y. Matsubara, "Analysis of carbides in multi-component white cast iron for hot rolling mill rolls," ISIJ International, vol. 44, no. 2, pp. 372-380, 2004.
Y. Yokomizo, N. Sasaguri, K. Nanjo, and Y. Matsubara, "Relationship between continuous cooling transformation behavior and chromium content of multi-component white cast iron," Journal of Japan Foundry Engineering Society, vol. 74, no. 11, pp. 691- 698, 2002.
M. Hashimoto, O. Kubo, N. Sasaguri, and Y. Matsubara, "Analysis of precipitated carbides in matrix of multi-component white cast iron," Journal of Japan Foundry Engineering Society, vol. 76, no. 3, pp. 205- 211, 2004.
A. Chooprajong, P. Sricharoenchai, S. Inthidech, and Y. Matsubara, "Three-bodytype abrasive wear behavior of 26% Cr cast iron with molybdenum," Journal of Metals, Materials and Minerals, vol. 22, pp. 31-37, 2012.
ดาวน์โหลด
เผยแพร่แล้ว
วิธีการอ้างอิง
ฉบับ
บท
การอนุญาต
ลิขสิทธิ์ (c) 2018 Journal of Metals, Materials and Minerals
This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.
Authors who publish in this journal agree to the following terms:
- Authors retain copyright and grant the journal right of first publication with the work simultaneously licensed under a Creative Commons Attribution License that allows others to share the work with an acknowledgment of the work's authorship and initial publication in this journal.
- Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgment of its initial publication in this journal.