X-Ray attenuation of cotton fabrics coated with barium sulphate

ผู้แต่ง

  • Boonsri Kusuktham Division of Textile Chemical Engineering, Faculty of Textile Industries, Rajamangala University of Technology Krungthep, Bangkok 10120, Thailand
  • Chavachot Wichayasiri Faculty of Textile Industries, Rajamangala University of Technology Krungthep
  • Somchai Udon Faculty of Textile Industries, Rajamangala University of Technology Krungthep

คำสำคัญ:

Barium sulfate, X-ray, Coating, Attenuation radiation ratio, Shielding

บทคัดย่อ

The x-ray attenuation performance of barium sulphate coated cotton fabrics was evaluated. 10-50 wt% barium sulphate/binder mixture was prepared and then coated onto cotton fabrics. For x-ray shielding evaluation, the fabrics with the different layers were tested under the x-ray radiation at 50kV-100 kV energy levels. The results showed that the shielding x-ray radiation were in the range of 1.48-77%, indicating that x-ray attenuation significantly increased with an increase in BaSO4 content. In addition, the number of fabric layers also played an important role. Finally, it was found that BaSO4 coated cotton fabrics exhibited satisfactory durability with respect to rubbing and washing tests.

Downloads

Download data is not yet available.

ประวัติผู้แต่ง

Boonsri Kusuktham, Division of Textile Chemical Engineering, Faculty of Textile Industries, Rajamangala University of Technology Krungthep, Bangkok 10120, Thailand

Division of Textile Chemical Engineering, Faculty of Textile Industries, Rajamangala University of Technology Krungthep

เอกสารอ้างอิง

Akkuri, I., Emikonel, S., Akarslan, F., Gunoglu, K. and Kilincarslan, S. (2015). Barite effect on radiation shielding properties of cottonpolyester fabric. Acta Physica Polonica A. 128 (2-B): B53-B54.

Aral, N., Negis, F.B. and Candan, C. (2016). An alternative x-ray shielding material based on coated textiles. Textile Res. J. 86 (8): 803-811.

Nambiar, S. and Yeow, J.T.W. (2012). Polymercomposite materials for radiation protechtion. ACS Appl. Mater. Interfaces. 4 (11): 5717- 5726.

Sla, L. Kaminskaia, N.M., Beniaev,N.E., Suslova, V. and Grigor’evskaia, M.S. (2012). The possibility of using inorganic fillers and matrix polymers in materials for radiation. J of Med. Tech. Nov-Dec (6): 10-13.

McCaffrey, J.P., Tessier, F. and Shen,H. (2012). Radiation shielding materiala and radiation scatter effects for intervention radiology (IR) physicians. Am. Assoc. Phys. Med. 39(7): 4537-4541.

Erdem, M., Baykara,O., Dogeu,M. and Kuluozturk, F. (2010). A novel shielding material prepared from solid waste containing lead for gamma ray. Radiation Phy. And Chem. 79(3): 917-922.

Zhong,W.H., Sui,G., Jana,S. and Miller,J. (2009). Comic radiation shielding tests for UHMWPE fiber/nano-epoxy composites. Comp. Sci and Tech. 69: 2093-2097.

CakiroGlu, M.A. (2016). Investigation of radiation shielding properties of polypropylene fiber reinforced shotcrete. Acta Physica Polonica A. 129 (4): 705-709.

Kilincarslan, S., Akkuri, I., Uncu,I.S. and Akarslan, F. (2016). Determination of radiation shielding properties of cotton polyester blend fabric coated with different barite rate. Acta Physica Polonica A. 129 (4): 878-879.

Vejakupta, K. and Udompataikul. (2014). Umbrella with ultraviolet radiation. J of Cosmetics, Dermatological Sci. and Appli. 4 (1) : 228-233.

Noppavan, C. and Ulumma, M. (2554). Nanofib composite mat for x-ray shielding. Science and Nucleartechnology Conferences 12th. : 1-6.

Kim, S.C. and Jung, H.M. (2013). A study on performance of low-dose medical radiation shielding fiber (RSF) in CT scans. Inter. J.Tech. 2 (1): 178-187.

Akarslan, F. Molla,T., Akkurt, I., Kilincarslan, S. and Uncu, I.S. Radiation Protection by the barite coated fabrics via image processing methodology. Acta Physica Polonica A. 125 (2): 316-318.

Omar, K., Al-Khazaleh, K.A. and Saadi, S.A. (2015). Barium sulfate epoxy mixture effects on attenuation of shoet wavelength radiation. Nuclear and radiation Phy. 80: 31333- 31338.

Aral, N. Nergls, F. B. and Candan,C. (2016). Investigation of x-ray attenuation and the flex resistance properties of fabrics coated with tungsten and barium sulphate additives. Tekstil ve Konfekslyon. 26 (2): 166-171.

ดาวน์โหลด

เผยแพร่แล้ว

2016-06-30

วิธีการอ้างอิง

[1]
B. . Kusuktham, C. Wichayasiri, และ S. Udon, “X-Ray attenuation of cotton fabrics coated with barium sulphate”, J Met Mater Miner, ปี 26, ฉบับที่ 1, มิ.ย. 2016.

ฉบับ

ปีที่ 26 ฉบับที่ 1 (2016)

บท

Original Research Articles

การอนุญาต

ลิขสิทธิ์ (c) 2017 วารสารโลหะ, วัสดุ และแร่

Creative Commons License

This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Authors who publish in this journal agree to the following terms:

    1. Authors retain copyright and grant the journal right of first publication with the work simultaneously licensed under a Creative Commons Attribution License that allows others to share the work with an acknowledgment of the work's authorship and initial publication in this journal.

 

    1. Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgment of its initial publication in this journal.