Morphology controlled calcium ortho phosphates induced by chemical additions under hydrothermal reaction
คำสำคัญ:
Calcium Phosphate, Hydroxyapatite, Whisker, Hydrothermalบทคัดย่อ
Morphology controlled calcium orthophosphates under hydrothermal reaction was achieved using saturated solution of monocalcium phosphate monohydrate (MCPM) as a starting material. MCPM saturated solution was hydrothermally treated at 180°C for 4 and 12 hrs. Citric acid as a chelating agent and a mixed solution of NaNO3and NaF were individually added into the reactor. The morphologies, phases and microstructures of the obtained products were characterized by optical microscope (OM), X-ray diffraction (XRD) and scanning electron microscope (SEM), respectively. Irregular shape crystals were obtained when a saturated solution of MCPM was autoclaved at 180°C for 4 hrs. Though citric acid was added into the reaction, the irregular shape products were still obtained with a minority of hexagonal plate crystals. As a result, the whiskers were synthesized when the mixed solution of NaNO3+ NaF was added into MCPM saturated solution and treated at 180°C for 12 hrs. Although the reaction time decreased from 12 to 4 hrs, the whisker products were still obtained. Phase analyses clarified by XRD that the whiskers were hydroxyapatite.##plugins.generic.usageStats.downloads##
เอกสารอ้างอิง
Elliot, J.C. 1994. Structure and chemistry of the apatites and other calcium orthophosphates. Amsterdam : Elsevier : 1-3.
Yoshimura, M., Suda, H., Okamoto, K., and Ioku, K. 1994. Hydrothermal synthesis of biocompatible whiskers. J. Mater. Sci, 29 : 3399-3402.
Suchanek, W., Suda, H., Yashima, M., Kakihana, M., and Yoshimura, M. 1995. Biocompatible whiskers with controlled morphology and stoichiometry. J. Mater. Res. 10(3) : 521-529.
Jinawath, S., Pongkao, D., Suchanek, W., and Yoshimura, M. 2001. Hydrothermal synthesis of monetite and hydroxyapatite from monocalcium phosphate monohydrate. J. Inorg. Mater. 3 : 997-1001.
Jinawath, S., Pongkao, D., and Yoshimura, M. 2002. Hydrothermal synthesis of hydroxyapatite from natural bone. J. Mater. Sci. Mater. Med. 13 : 491-494.
Jinawath, S., Polchai, D., and Yoshimura, M. 2002. Low-temperature hydrothermal transformation of aragonite to hydroxyapatite. Mater. Sci. Eng. C. 13 : 35-39.
Monma, H. 1993. Electrochemical deposition of calcium-deficient apatite on stainless steel substrate. Jpn.J.Ceram.Soc. 101(7) : 737- 739.
LeGeros, R.Z. 1991. Calcium phosphates in oral biology and medicine. In : Monograph in oral science, Myers, H.M. (ed.) Basel : Karger : 83-87.
Aoba, T. 1997. The effect of fluoride on apatite structure and growth. Crit. Rev. Oral Biol. Med. 8 : 136-153.
LeGeros, R.Z., Mijares, D., Yao, F., LeGeros, J.P., Bromage, T., La, V., Xi, Q., Tannous, S., and Kijkowska, R. 2006. Consequence of fluoride incorporation on properties of apatites. Key. Eng. Mater. 309-311 : 697- 700.
ดาวน์โหลด
เผยแพร่แล้ว
วิธีการอ้างอิง
ฉบับ
บท
การอนุญาต
ลิขสิทธิ์ (c) 2017 Journal of Metals, Materials and Minerals
![Creative Commons License](http://i.creativecommons.org/l/by-nc-nd/4.0/88x31.png)
This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.
Authors who publish in this journal agree to the following terms:
- Authors retain copyright and grant the journal right of first publication with the work simultaneously licensed under a Creative Commons Attribution License that allows others to share the work with an acknowledgment of the work's authorship and initial publication in this journal.
- Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgment of its initial publication in this journal.