Aluminium-SiC composite: Study of its mechanical properties
คำสำคัญ:
Composite materials, Indentation and hardness, Tensile properties, Deformation and fractureบทคัดย่อ
Cylindrical specimens with geometries and sizes, in agreement with the standard of American Society for Testing Materials (ASTM), they were used to characterize the tension behaviour of the composite. A significant effect of the SiC shape/size on the tensile behaviour of aluminium-based composite was observed, caused by the differences between the superheat (993 K) and the mould temperatures (333 K, 473 K, 623 K) in the melting practice. Ultimate tensile stress and Fracture Toughness factor for the composite showed a numerical advantage over the corresponding ones to the aluminium at a solidification speed of 82.5 K·s-1. At the mould temperature of 473 K, ultimate tensile stress decreased 8.9 % meanwhile Fracture Toughness factor increased 4.3 %. For mould temperatures higher than 473 K the size and number of SiC-clusters determined the tension behaviour of the specimens. High hardness values are obtained with high cooling rates (82.5 K·s-1) and it diminishes gradually as the cooling speed decreases for both sizes of particles.Downloads
เอกสารอ้างอิง
R. Behera, N. R. Mohanta, and G. Sutradhar, "Distribution of SiC particulates in stir cast aluminium alloy metal matrix composites and its effect on mechanical properties," International Journal of Emerging trends in Engineering and Development, vol. 1, pp. 194- 205, 2012.
M. K. Surappa and P. K. Rohatgi, "Preparation and properties of cast aluminium-ceramic particle composites," Journal of Materials Science, vol. 16, pp. 983-993, 1981.
V. Kevorkijan, Z. I. Raziskovalec, A. Kategorije, and B. Suštaršič, "The introduction of fine SiC particles into a molten Al alloy matrix: Application to composite material casting, "Kovine, zlitine, Tehnologije, vol. 39, pp. 447-454, 1995.
J. Hashim, "The production of cast metal matrix composite by a modified stir casting method," Jurnal Teknologi, vol. 35, pp.9-20, 2001.
D. S. Prasad, C. Shoba, and N. Ramanaiah, "Investigations on mechanical properties of aluminum hybrid composites," Journal of Materials Research and Technology, vol. 31, pp. 79-85, 2014.
S. Tzamtzis, N. Barekar, H. Nadendla, J. Patel, B. Dhindaw, and Z. Fan, "Processing of advanced Al/SiC particulate metal matrix composites under intensive shearing - a novel Rheo-process," Composites Part A: Applied Science and Manufacturing, vol. 40, pp.144- 151, 2009.
J. Roy, S. Chandra, S. Das, and S. Maitra, "Oxidation behavior of silicon carbide-A review," Reviews on Advanced Materials Science, vol. 38, pp. 29-39, 2014.
R. N. Ibrahim and H. L. "Stark, Validity requirements for fracture toughness measurements obtained from small circumferentially notched cylindrical specimens," Engineering Fracture Machanics, vol. 28, pp. 455-460, 1987.
K. K. Chawla, Composite Materials :Science and Engineering. New York: SpringerVerlag New York, 2012.
M. C. Flemings, Solidification Processing. United States of America: McGraw-Hill Inc., 1974.
ดาวน์โหลด
เผยแพร่แล้ว
วิธีการอ้างอิง
ฉบับ
บท
การอนุญาต
ลิขสิทธิ์ (c) 2018 Journal of Metals, Materials and Minerals
This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.
Authors who publish in this journal agree to the following terms:
- Authors retain copyright and grant the journal right of first publication with the work simultaneously licensed under a Creative Commons Attribution License that allows others to share the work with an acknowledgment of the work's authorship and initial publication in this journal.
- Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgment of its initial publication in this journal.