Microstructural characterization of aluminum powder liquid coating on IN 738 superalloy

ผู้แต่ง

  • Patama Visuttipitukul Department of Metallurgical Engineering, Chulalongkorn University
  • Nuntiya Limvanutpong Department of Metallurgical Engineering, Chulalongkorn University
  • Viyaporn Krongtong National Metal and Materials Technology Center (MTEC), Bangkok
  • Panyawat Wangyao etallurgy and Materials Science Research Institute (MMRI), Chulalongkorn University

บทคัดย่อ

The powder liquid coating method was proposed for aluminizing of nickel-based superalloy grade IN738 in this study. Slurries for the coating consisted of aluminum and alumina (Al2O3) powder with various weight ratios in the range from 3:7 to 10:0. The slurries were pasted onto the IN738 specimens, which were subsequently dried and heated under argon atmosphere. Macrostructures of coated samples were observed. Surface and cross-sectional microstructures were studied by OM and SEM. Qualitative analysis and composition mapping were analyzed by EDS. Phase identification of coated surface was done by GIXD, at the incident angle of 2 degrees. The results showed inhomogeneous formation of Ni2Al3 on the coated surface. The Ni2Al3 phase had the structure of dispersed nodular islands and of thin discontinuous layer on flat area. Size and amount of nodular islands were larger when the ratio of Al:Al2O3 increased. Therefore, the amount of Ni2Al3 formation was increased with the ratio of Al:Al2O3. These nodular islands were formed due to the low wettability of liquid aluminum on nickel surface. Some aluminum oxide and chromium oxide were found in coexistence with Ni2Al3.

Downloads

Download data is not yet available.

เอกสารอ้างอิง

Pomeroy, M. J. 2005. Mater. Design 26 : 223-231.

Cheruvu, N. S. 2000. Proceeding of 2000 International Joint Power Generation Conference, July 23-26 : 1-8.

Murakami, K., Nishida, N., Osamura, K. and Tomota, Y. 2004. Aluminization of High Purity Iron by Powder Liquid Coating. Acta Mater. 52 : 1271-1281.

Houngninou, C., Chevalier, S. and Larpin, J. P. 2004. Synthesis and Characterisation of Pack Cemented Aluminide Coatings on Metals. Appl. Surface Sci. 236 : 256-269.

Chien, A., Gan, D. and Shen, P. 1996. Microstructures of Two-Stage Aluminized Coatings on Inconel 600. Mater. Sci. Eng. A206 : 215-224.

Ip, S. W., Sridhar, R., Toguri, J.M., Stephenson, T.F. and Warner, A. E. M. 1998. Wettability of Nickel Coated Graphite by Aluminum. Mater. Sci. Eng. A244 : 31-38.

ดาวน์โหลด

เผยแพร่แล้ว

2017-04-23

วิธีการอ้างอิง

[1]
P. . Visuttipitukul, N. Limvanutpong, V. Krongtong, และ P. Wangyao, “Microstructural characterization of aluminum powder liquid coating on IN 738 superalloy”, J Met Mater Miner, ปี 17, ฉบับที่ 1, เม.ย. 2017.

ฉบับ

ปีที่ 17 ฉบับที่ 1 (2007)

บท

Original Research Articles

การอนุญาต

ลิขสิทธิ์ (c) 2017 Journal of Metals, Materials and Minerals

Creative Commons License

This work is licensed under a Creative Commons Attribution-NonCommercial-NoDerivatives 4.0 International License.

Authors who publish in this journal agree to the following terms:

    1. Authors retain copyright and grant the journal right of first publication with the work simultaneously licensed under a Creative Commons Attribution License that allows others to share the work with an acknowledgment of the work's authorship and initial publication in this journal.

 

    1. Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgment of its initial publication in this journal.

Most read articles by the same author(s)

<< < 1 2 3 4 > >>